Neoprene latex mortar

1. The mortar has excellent adhesion and is strong in terms of crack resistance, frost resistance, anti-seepage, anti-corrosion, anti-chloride ion penetration, abrasion resistance, aging resistance, etc.
2. It is suitable for anti-seepage, anti-corrosion protection and repair projects of water conservancy projects, port engineering, highway, bridge, metallurgy, chemical industry, industrial and civil buildings and other steel structures and reinforced concrete structures.

Focusing on measuring solid content

Test Items	Cationic Neoprene Latex
Appearance	Milky white uniform emulsion
Viscosity (applying 4 cups, 25°C, s)	12.0-15.5
Total solid content (%)	47-52
Density (g/m3)	≥1.080
Storage stability	5°C -40°C, no obvious precipitation in 3 months

Test items / Neoprene Latex Cement Mortar

Compressive strength MPa, ≥	Tensile strength MPa, ≥	Bonding strength MPa, ≥	Impermeability grade MPa, ≥	water absorption (%), ≤	Applicable temperature (°C), ≤
20	3.0	1.2 with cement substrate; 2.0 with steel substrate	1.5	4.0	60

RF cationic neoprene latex waterproof and anticorrosive mortar is mixed by high molecular polymer emulsion, special cementing materials, and high-quality aggregates according to a special process.

Keywords:

building materials

classification:

Polymer-modified mortar

Usage:

1. The concrete strengthening of building structure, and waterproof and leak-proof of the air defense facilities.
2. Seepage prevention treatment for reservoir dams and ports.
3. Chemical corrosion-proof buildings such as thermal pools, landfills, chemical warehouses, chemical tanks, etc.
4. Concrete repair of roads, bridge decks, tunnels and culverts.
5. Anti-leakage treatment for roofs, bathrooms and basements of industrial and civil buildings.
6. Waterproof of steel structure and steel concrete.
7. It can be directly applied on the wet base surface, and has good adhesion to a variety of substrates.

Advantage

Product detail

Focusing on measuring solid content

Test Items	Cationic Neoprene Latex
Appearance	Milky white uniform emulsion
Viscosity (applying 4 cups, 25°C, s)	12.0-15.5
Total solid content (%)	47-52
Density (g/m3)	≥1.080
Storage stability	5°C -40°C, no obvious precipitation in 3 months

Test items / Neoprene Latex Cement Mortar

Compressive strength MPa, ≥	Tensile strength MPa, ≥	Bonding strength MPa, ≥	Impermeability grade MPa, ≥	water absorption (%), ≤	Applicable temperature (°C), ≤
20	3.0	1.2 with cement substrate; 2.0 with steel substrate	1.5	4.0	60

概要

RF cationic neoprene latex waterproof and anticorrosive mortar is mixed by high molecular polymer emulsion, special cementing materials, and high-quality aggregates according to a special process.

Advantage

Product detail

Focusing on measuring solid content

Test Items	Cationic Neoprene Latex
Appearance	Milky white uniform emulsion
Viscosity (applying 4 cups, 25°C, s)	12.0-15.5
Total solid content (%)	47-52
Density (g/m3)	≥1.080
Storage stability	5°C -40°C, no obvious precipitation in 3 months

Test items / Neoprene Latex Cement Mortar

Compressive strength MPa, ≥	Tensile strength MPa, ≥	Bonding strength MPa, ≥	Impermeability grade MPa, ≥	water absorption (%), ≤	Applicable temperature (°C), ≤
20	3.0	1.2 with cement substrate; 2.0 with steel substrate	1.5	4.0	60

概要

RF cationic neoprene latex waterproof and anticorrosive mortar is mixed by high molecular polymer emulsion, special cementing materials, and high-quality aggregates according to a special process.

Documents

High strength non shrinkage grouting material for CBGM-5 suction cylinder

Download

CBGM low-temperature prefabricated wind power special grouting material

Download

Underwater anti dispersion grouting material for CBGM offshore wind power

Download

< 1 >

Online Message

Need help?

Let's ask your questions