SMA100 Heavy-duty impact resistant floor hardener
SMA100 Heavy-duty impact resistant floor hardener
Performance metrics
|
Item |
Index |
|
Wear-resistance |
0.012g/cm2 (Gear method) |
|
Oil-resistance |
The strength of oil bubble does not decrease for three years, and the oil permeability is less than 0.3mm (including impermeability) |
|
Compressive strength |
≥90MPa |
|
Flexural strength (28d) |
>11.5MPa (not broken) |
|
Tensile strength |
3.5MPa |
Construction process
Base surface treatment:
The base course shall be flat and solid, dust, oil stain, etc. on the surface shall be removed, the leaking parts shall be treated with plugging materials first, and the periphery of the parts in contact with different materials of metal and plastic pipes shall be polished. When the base course is too dry, it can be watered first, and the later construction can be carried out when there is no water.
SMA100 material configuration:
According to the proportion of 100kg dry material and 8kg water, it can be used by hand-held electric mixer or manual mixing. The prepared SMA100 should be used up within 1 hour at room temperature.
SMA100 Construction:
1. Layered construction is required. The thickness of one construction shall not be greater than 10mm. After the initial setting of the front layer, the layer shall be plastered until the design thickness.
2. Watering maintenance shall be carried out 24 hours after construction. The maintenance time depends on the temperature conditions on site, and it is appropriate to take 3 ~ 5 days at normal temperature.
◆ Places with high heavy load, high wear-resistance and high impact-resistance
◆ Places resistant to oil seepage
◆ Reconstruction of old concrete floor
SMA100 heavy-duty impact resistant floor hardener, through double high composite anti rust, makes the ground have the characteristics of anti-rust, impact-resistance, corrosion-resistance of weak acid and weak alkali. Through scientific aggregate grading and construction methods, the thickest part of the concrete surface can reach 12mm. So as to enhance the wear resistance and impact resistance of concrete surface. Laid on general concrete surface. Synchronous construction with concrete surface. Make the material and concrete form a whole and become an industrial floor with special wear-resistance and impact-resistance.
Keywords:
classification:
SMA100 heavy-duty impact resistant floor hardener, through double high composite anti rust, makes the ground have the characteristics of anti-rust, impact-resistance, corrosion-resistance of weak acid and weak alkali. Through scientific aggregate grading and construction methods, the thickest part of the concrete surface can reach 12mm. So as to enhance the wear resistance and impact resistance of concrete surface. Laid on general concrete surface. Synchronous construction with concrete surface. Make the material and concrete form a whole and become an industrial floor with special wear-resistance and impact-resistance.
Product features
◆ With extremely high hardness and toughness
◆ Can meet the requirements of smooth and anti-skid
◆ With excellent impermeability, rust-resistance, salt alkali-resistance and weak acid-resistance
◆ The old ground reconstruction process is simple and the construction period is short
Packaging and storage
Packed in PP bags, with a net weight of 25kg / bag and a shelf life of 3 months; It must be stored in a dry and ventilated room, and the packaging bag shall be sealed. Avoid moisture and freeze.
Performance metrics
|
Item |
Index |
|
Wear-resistance |
0.012g/cm2 (Gear method) |
|
Oil-resistance |
The strength of oil bubble does not decrease for three years, and the oil permeability is less than 0.3mm (including impermeability) |
|
Compressive strength |
≥90MPa |
|
Flexural strength (28d) |
>11.5MPa (not broken) |
|
Tensile strength |
3.5MPa |
Construction process
Base surface treatment:
The base course shall be flat and solid, dust, oil stain, etc. on the surface shall be removed, the leaking parts shall be treated with plugging materials first, and the periphery of the parts in contact with different materials of metal and plastic pipes shall be polished. When the base course is too dry, it can be watered first, and the later construction can be carried out when there is no water.
SMA100 material configuration:
According to the proportion of 100kg dry material and 8kg water, it can be used by hand-held electric mixer or manual mixing. The prepared SMA100 should be used up within 1 hour at room temperature.
SMA100 Construction:
1. Layered construction is required. The thickness of one construction shall not be greater than 10mm. After the initial setting of the front layer, the layer shall be plastered until the design thickness.
2. Watering maintenance shall be carried out 24 hours after construction. The maintenance time depends on the temperature conditions on site, and it is appropriate to take 3 ~ 5 days at normal temperature.
◆ Places with high heavy load, high wear-resistance and high impact-resistance
◆ Places resistant to oil seepage
◆ Reconstruction of old concrete floor
SMA100 heavy-duty impact resistant floor hardener, through double high composite anti rust, makes the ground have the characteristics of anti-rust, impact-resistance, corrosion-resistance of weak acid and weak alkali. Through scientific aggregate grading and construction methods, the thickest part of the concrete surface can reach 12mm. So as to enhance the wear resistance and impact resistance of concrete surface. Laid on general concrete surface. Synchronous construction with concrete surface. Make the material and concrete form a whole and become an industrial floor with special wear-resistance and impact-resistance.
Performance metrics
|
Item |
Index |
|
Wear-resistance |
0.012g/cm2 (Gear method) |
|
Oil-resistance |
The strength of oil bubble does not decrease for three years, and the oil permeability is less than 0.3mm (including impermeability) |
|
Compressive strength |
≥90MPa |
|
Flexural strength (28d) |
>11.5MPa (not broken) |
|
Tensile strength |
3.5MPa |
Construction process
Base surface treatment:
The base course shall be flat and solid, dust, oil stain, etc. on the surface shall be removed, the leaking parts shall be treated with plugging materials first, and the periphery of the parts in contact with different materials of metal and plastic pipes shall be polished. When the base course is too dry, it can be watered first, and the later construction can be carried out when there is no water.
SMA100 material configuration:
According to the proportion of 100kg dry material and 8kg water, it can be used by hand-held electric mixer or manual mixing. The prepared SMA100 should be used up within 1 hour at room temperature.
SMA100 Construction:
1. Layered construction is required. The thickness of one construction shall not be greater than 10mm. After the initial setting of the front layer, the layer shall be plastered until the design thickness.
2. Watering maintenance shall be carried out 24 hours after construction. The maintenance time depends on the temperature conditions on site, and it is appropriate to take 3 ~ 5 days at normal temperature.
◆ Places with high heavy load, high wear-resistance and high impact-resistance
◆ Places resistant to oil seepage
◆ Reconstruction of old concrete floor
SMA100 heavy-duty impact resistant floor hardener, through double high composite anti rust, makes the ground have the characteristics of anti-rust, impact-resistance, corrosion-resistance of weak acid and weak alkali. Through scientific aggregate grading and construction methods, the thickest part of the concrete surface can reach 12mm. So as to enhance the wear resistance and impact resistance of concrete surface. Laid on general concrete surface. Synchronous construction with concrete surface. Make the material and concrete form a whole and become an industrial floor with special wear-resistance and impact-resistance.
Documents
Online Message
Need help?
Let's ask your questions
Related Product Recommendations
undefined
Product Documentation
If you do not have a comprehensive understanding of our products, we have uploaded relevant technical documents for you to download and reference so that you can better understand our product usage and technical parameters
View More
Cooperation Case
Online Message