JGN802 Carbon Fiber Adhesive
JGN802 Carbon Fiber Adhesive
◆ The adhesive has good wettability and permeability, and the composite material formed by the adhesive and carbon fiber sheet has strong mechanical properties and excellent durability. The adhesive also has good thixotropy properties and good suspension, making the vertical surface construction less fluidity.
◆ The cured adhesive layer has excellent physical and mechanical properties, strength and toughness.
◆ This adhesive has good performance in anti-aging and medium resistance (acid, alkali, water).
◆ The adhesive can be cured at room temperature, and it does not contain volatile solvents. It is non-toxic and environmentally friendly, and has high bonding strength.
◆ The proportion of adhesive is loose, and the temperature can be adjusted appropriately for different ambient temperatures. The adhesive is easy to use and easy to operate on site.
Category I Grade A Adhesive of GB50278-2011 Technical Code for Safety Appraisal of Engineering Structural Strengthening Materials
|
|
Performance item |
Performance requirement |
|
Colloidal Performance |
Tensile strength (MPa) |
≥38 |
|
Tensile elastic modulus (MPa) |
≥2.4×103 |
|
|
Elongation (%) |
≥1.5 |
|
|
Flexural strength (MPa) |
≥50 |
|
|
And it cannot be cracked. |
||
|
Compressive strength (MPa) |
≥70 |
|
|
Adhesion performance |
Standard value of Steel-steel tensile shear strength (MPa) |
≥14 |
|
Steel-steel bond tensile strength (MPa) |
≥40 |
|
|
Steel-steel T impact stripping length (mm) |
≤20 |
|
|
Positive tensile bond strength of steel-C45 concrete (MPa) |
≥2.5, and it is a cohesive failure of concrete. |
|
|
|
Non-volatile content (solid content) (%) |
≥99 |
two-component modified epoxy Carbon Fiber adhesive for the composite system strengthening the concrete
Keywords:
classification:
Usage:
◆ Used for painting the bottom layer on the surface of the strengthening structural parts.
◆ Used for repairing and leveling the defects on the surface of strengthening structural parts.
◆ Used for impregnation and pasting of carbon fiber, glass fiber and other fiber sheets on the surface of the strengthening structural parts.
◆ The adhesive has good wettability and permeability, and the composite material formed by the adhesive and carbon fiber sheet has strong mechanical properties and excellent durability. The adhesive also has good thixotropy properties and good suspension, making the vertical surface construction less fluidity.
◆ The cured adhesive layer has excellent physical and mechanical properties, strength and toughness.
◆ This adhesive has good performance in anti-aging and medium resistance (acid, alkali, water).
◆ The adhesive can be cured at room temperature, and it does not contain volatile solvents. It is non-toxic and environmentally friendly, and has high bonding strength.
◆ The proportion of adhesive is loose, and the temperature can be adjusted appropriately for different ambient temperatures. The adhesive is easy to use and easy to operate on site.
Category I Grade A Adhesive of GB50278-2011 Technical Code for Safety Appraisal of Engineering Structural Strengthening Materials
|
|
Performance item |
Performance requirement |
|
Colloidal Performance |
Tensile strength (MPa) |
≥38 |
|
Tensile elastic modulus (MPa) |
≥2.4×103 |
|
|
Elongation (%) |
≥1.5 |
|
|
Flexural strength (MPa) |
≥50 |
|
|
And it cannot be cracked. |
||
|
Compressive strength (MPa) |
≥70 |
|
|
Adhesion performance |
Standard value of Steel-steel tensile shear strength (MPa) |
≥14 |
|
Steel-steel bond tensile strength (MPa) |
≥40 |
|
|
Steel-steel T impact stripping length (mm) |
≤20 |
|
|
Positive tensile bond strength of steel-C45 concrete (MPa) |
≥2.5, and it is a cohesive failure of concrete. |
|
|
|
Non-volatile content (solid content) (%) |
≥99 |
two-component modified epoxy Carbon Fiber adhesive for the composite system strengthening the concrete
◆ The adhesive has good wettability and permeability, and the composite material formed by the adhesive and carbon fiber sheet has strong mechanical properties and excellent durability. The adhesive also has good thixotropy properties and good suspension, making the vertical surface construction less fluidity.
◆ The cured adhesive layer has excellent physical and mechanical properties, strength and toughness.
◆ This adhesive has good performance in anti-aging and medium resistance (acid, alkali, water).
◆ The adhesive can be cured at room temperature, and it does not contain volatile solvents. It is non-toxic and environmentally friendly, and has high bonding strength.
◆ The proportion of adhesive is loose, and the temperature can be adjusted appropriately for different ambient temperatures. The adhesive is easy to use and easy to operate on site.
Category I Grade A Adhesive of GB50278-2011 Technical Code for Safety Appraisal of Engineering Structural Strengthening Materials
|
|
Performance item |
Performance requirement |
|
Colloidal Performance |
Tensile strength (MPa) |
≥38 |
|
Tensile elastic modulus (MPa) |
≥2.4×103 |
|
|
Elongation (%) |
≥1.5 |
|
|
Flexural strength (MPa) |
≥50 |
|
|
And it cannot be cracked. |
||
|
Compressive strength (MPa) |
≥70 |
|
|
Adhesion performance |
Standard value of Steel-steel tensile shear strength (MPa) |
≥14 |
|
Steel-steel bond tensile strength (MPa) |
≥40 |
|
|
Steel-steel T impact stripping length (mm) |
≤20 |
|
|
Positive tensile bond strength of steel-C45 concrete (MPa) |
≥2.5, and it is a cohesive failure of concrete. |
|
|
|
Non-volatile content (solid content) (%) |
≥99 |
two-component modified epoxy Carbon Fiber adhesive for the composite system strengthening the concrete
Documents
Online Message
Need help?
Let's ask your questions
Related Product Recommendations
undefined
Product Documentation
If you do not have a comprehensive understanding of our products, we have uploaded relevant technical documents for you to download and reference so that you can better understand our product usage and technical parameters
View More
Cooperation Case
Online Message